The effect of cataphoretic and powder coatings on the strength and failure modes of EN AW-5754 aluminium alloy adhesive joints

Author
Organization
Abstract
The aim of this study is to determine the effect of cataphoretic and powder coatings and also the method of application the primer on the adherends surface on the strength and failure modes of EN AW-5754 aluminium alloy adhesive joints. The study is performed on lap joints made of EN AW-5754 aluminium alloy, subjected to three different types of surface treatment; namely a) polyurethane cataphoretic coating, b) powder coating based on black mat RAL 9005 UL polyester resin and c) no coating. The tested adhesive joints were made using a one component polyurethane adhesive Terostat 8596, which was dedicated for automotive and cured under a constant load of 0.018 MPa at 20 +/- 2 degrees C. In addition, this study investigates the effect of the application of Terostat 8519P adhesion promoter which is a liquid polyurethane-based primer containing solvents and which is corresponding to Terostat 8596 polyurethane adhesive. Terostat 8519P adhesion promoter was applied in two different ways: a) to one substrate and b) to both substrates. The produced adhesive joints were subjected to strength tests using the Zwick/Roell Z150 testing machine. The examination of fracture in the tested adhesive joints was performed in accordance with the EN ISO 10365 standard. The shear strength results have demonstrated that both the method of application of the adhesion promoter (Terostat 8519 P) and the presence of cataphoretic coating had an influence on adhesive joints strength. The use of the adhesion promoter significantly affects the strength of both uncoated EN AW-5754 aluminium alloy adhesive joints and the adhesive joints subjected to powder coating. The use of the adhesion promoter has a less significant effect on the cataphoretic-coated samples.
Keywords
General Chemical Engineering, Polymers and Plastics, Biomaterials, Adhesive joints, Aluminium and alloys, Surface treatment, Coating, SURFACE PRETREATMENT, BOND STRENGTH, DURABILITY, PRIMERS, ENERGY

Downloads

  • (...).pdf
    • full text (Published version)
    • |
    • UGent only
    • |
    • PDF
    • |
    • 6.73 MB

Citation

Please use this url to cite or link to this publication:

MLA
Rudawska, Anna, and Magd Abdel Wahab. “The Effect of Cataphoretic and Powder Coatings on the Strength and Failure Modes of EN AW-5754 Aluminium Alloy Adhesive Joints.” INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, vol. 89, 2019, pp. 40–50.
APA
Rudawska, A., & Abdel Wahab, M. (2019). The effect of cataphoretic and powder coatings on the strength and failure modes of EN AW-5754 aluminium alloy adhesive joints. INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 89, 40–50.
Chicago author-date
Rudawska, Anna, and Magd Abdel Wahab. 2019. “The Effect of Cataphoretic and Powder Coatings on the Strength and Failure Modes of EN AW-5754 Aluminium Alloy Adhesive Joints.” INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES 89: 40–50.
Chicago author-date (all authors)
Rudawska, Anna, and Magd Abdel Wahab. 2019. “The Effect of Cataphoretic and Powder Coatings on the Strength and Failure Modes of EN AW-5754 Aluminium Alloy Adhesive Joints.” INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES 89: 40–50.
Vancouver
1.
Rudawska A, Abdel Wahab M. The effect of cataphoretic and powder coatings on the strength and failure modes of EN AW-5754 aluminium alloy adhesive joints. INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES. 2019;89:40–50.
IEEE
[1]
A. Rudawska and M. Abdel Wahab, “The effect of cataphoretic and powder coatings on the strength and failure modes of EN AW-5754 aluminium alloy adhesive joints,” INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, vol. 89, pp. 40–50, 2019.
@article{8599431,
  abstract     = {The aim of this study is to determine the effect of cataphoretic and powder coatings and also the method of application the primer on the adherends surface on the strength and failure modes of EN AW-5754 aluminium alloy adhesive joints. The study is performed on lap joints made of EN AW-5754 aluminium alloy, subjected to three different types of surface treatment; namely a) polyurethane cataphoretic coating, b) powder coating based on black mat RAL 9005 UL polyester resin and c) no coating. The tested adhesive joints were made using a one component polyurethane adhesive Terostat 8596, which was dedicated for automotive and cured under a constant load of 0.018 MPa at 20 +/- 2 degrees C. In addition, this study investigates the effect of the application of Terostat 8519P adhesion promoter which is a liquid polyurethane-based primer containing solvents and which is corresponding to Terostat 8596 polyurethane adhesive. Terostat 8519P adhesion promoter was applied in two different ways: a) to one substrate and b) to both substrates. The produced adhesive joints were subjected to strength tests using the Zwick/Roell Z150 testing machine. The examination of fracture in the tested adhesive joints was performed in accordance with the EN ISO 10365 standard. The shear strength results have demonstrated that both the method of application of the adhesion promoter (Terostat 8519 P) and the presence of cataphoretic coating had an influence on adhesive joints strength. The use of the adhesion promoter significantly affects the strength of both uncoated EN AW-5754 aluminium alloy adhesive joints and the adhesive joints subjected to powder coating. The use of the adhesion promoter has a less significant effect on the cataphoretic-coated samples.},
  author       = {Rudawska, Anna and Abdel Wahab, Magd},
  issn         = {0143-7496},
  journal      = {INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES},
  keywords     = {General Chemical Engineering,Polymers and Plastics,Biomaterials,Adhesive joints,Aluminium and alloys,Surface treatment,Coating,SURFACE PRETREATMENT,BOND STRENGTH,DURABILITY,PRIMERS,ENERGY},
  language     = {eng},
  pages        = {40--50},
  title        = {The effect of cataphoretic and powder coatings on the strength and failure modes of EN AW-5754 aluminium alloy adhesive joints},
  url          = {http://dx.doi.org/10.1016/j.ijadhadh.2018.11.005},
  volume       = {89},
  year         = {2019},
}

Altmetric
View in Altmetric
Web of Science
Times cited: