'Brown etching layer': a possible new insight into the crack initiation of rolling contact fatigue in rail steels?
- Author
- Shaoguang Li, Jun Wu, Roumen Petrov (UGent) , ZL Li, R Dollevoet and Jilt Sietsma (UGent)
- Organization
- Keywords
- White etching layer, Brown etching layer, Rolling contact fatigue, CEMENTITE, ELECTRON-MICROSCOPY, MECHANICAL-PROPERTIES, NANOCRYSTALLINE FERRITE, VALIDATION, Microstructural characterization, TEMPERATURES, SURFACE, PEARLITIC STEEL, CORRUGATED RAIL, SEVERE PLASTIC-DEFORMATION, Cracks
Downloads
-
(...).pdf
- full text
- |
- UGent only
- |
- |
- 3.56 MB
Citation
Please use this url to cite or link to this publication: http://hdl.handle.net/1854/LU-8052026
- MLA
- Li, Shaoguang, et al. “‘Brown Etching Layer’: A Possible New Insight into the Crack Initiation of Rolling Contact Fatigue in Rail Steels?” ENGINEERING FAILURE ANALYSIS, vol. 66, PERGAMON-ELSEVIER SCIENCE LTD, 2016, pp. 8–18, doi:10.1016/j.engfailanal.2016.03.019.
- APA
- Li, S., Wu, J., Petrov, R., Li, Z., Dollevoet, R., & Sietsma, J. (2016). “Brown etching layer”: a possible new insight into the crack initiation of rolling contact fatigue in rail steels? ENGINEERING FAILURE ANALYSIS, 66, 8–18. https://doi.org/10.1016/j.engfailanal.2016.03.019
- Chicago author-date
- Li, Shaoguang, Jun Wu, Roumen Petrov, ZL Li, R Dollevoet, and Jilt Sietsma. 2016. “‘Brown Etching Layer’: A Possible New Insight into the Crack Initiation of Rolling Contact Fatigue in Rail Steels?” ENGINEERING FAILURE ANALYSIS 66: 8–18. https://doi.org/10.1016/j.engfailanal.2016.03.019.
- Chicago author-date (all authors)
- Li, Shaoguang, Jun Wu, Roumen Petrov, ZL Li, R Dollevoet, and Jilt Sietsma. 2016. “‘Brown Etching Layer’: A Possible New Insight into the Crack Initiation of Rolling Contact Fatigue in Rail Steels?” ENGINEERING FAILURE ANALYSIS 66: 8–18. doi:10.1016/j.engfailanal.2016.03.019.
- Vancouver
- 1.Li S, Wu J, Petrov R, Li Z, Dollevoet R, Sietsma J. “Brown etching layer”: a possible new insight into the crack initiation of rolling contact fatigue in rail steels? ENGINEERING FAILURE ANALYSIS. 2016;66:8–18.
- IEEE
- [1]S. Li, J. Wu, R. Petrov, Z. Li, R. Dollevoet, and J. Sietsma, “‘Brown etching layer’: a possible new insight into the crack initiation of rolling contact fatigue in rail steels?,” ENGINEERING FAILURE ANALYSIS, vol. 66, pp. 8–18, 2016.
@article{8052026, author = {{Li, Shaoguang and Wu, Jun and Petrov, Roumen and Li, ZL and Dollevoet, R and Sietsma, Jilt}}, issn = {{1350-6307}}, journal = {{ENGINEERING FAILURE ANALYSIS}}, keywords = {{White etching layer,Brown etching layer,Rolling contact fatigue,CEMENTITE,ELECTRON-MICROSCOPY,MECHANICAL-PROPERTIES,NANOCRYSTALLINE FERRITE,VALIDATION,Microstructural characterization,TEMPERATURES,SURFACE,PEARLITIC STEEL,CORRUGATED RAIL,SEVERE PLASTIC-DEFORMATION,Cracks}}, language = {{eng}}, pages = {{8--18}}, publisher = {{PERGAMON-ELSEVIER SCIENCE LTD}}, title = {{'Brown etching layer': a possible new insight into the crack initiation of rolling contact fatigue in rail steels?}}, url = {{http://dx.doi.org/10.1016/j.engfailanal.2016.03.019}}, volume = {{66}}, year = {{2016}}, }
- Altmetric
- View in Altmetric
- Web of Science
- Times cited: