Internal and surface damage of multiphase steels and pure iron after electrochemical hydrogen charging

(2011) CORROSION SCIENCE. 53(10). p.3166-3176
Author
Organization
Keywords
STRESS-CORROSION CRACKING, INDUCED BLISTER CRACKING, HIGH-STRENGTH STEEL, INCLUSIONS, Iron, Steel, SEM, Hydrogen embrittlement, Segregation, NUCLEATION, ALUMINUM, PIPELINE STEELS, EMBRITTLEMENT, ABSORPTION, MECHANISM

Downloads

  • (...).pdf
    • full text
    • |
    • UGent only
    • |
    • PDF
    • |
    • 2.76 MB

Citation

Please use this url to cite or link to this publication:

Chicago
Perez Escobar, Diana Maria, C Minambres, L Duprez, Kim Verbeken, and Marc Verhaege. 2011. “Internal and Surface Damage of Multiphase Steels and Pure Iron After Electrochemical Hydrogen Charging.” Corrosion Science 53 (10): 3166–3176.
APA
Perez Escobar, D. M., Minambres, C., Duprez, L., Verbeken, K., & Verhaege, M. (2011). Internal and surface damage of multiphase steels and pure iron after electrochemical hydrogen charging. CORROSION SCIENCE, 53(10), 3166–3176.
Vancouver
1.
Perez Escobar DM, Minambres C, Duprez L, Verbeken K, Verhaege M. Internal and surface damage of multiphase steels and pure iron after electrochemical hydrogen charging. CORROSION SCIENCE. 2011;53(10):3166–76.
MLA
Perez Escobar, Diana Maria, C Minambres, L Duprez, et al. “Internal and Surface Damage of Multiphase Steels and Pure Iron After Electrochemical Hydrogen Charging.” CORROSION SCIENCE 53.10 (2011): 3166–3176. Print.
@article{2125740,
  author       = {Perez Escobar, Diana Maria and Minambres, C and Duprez, L and Verbeken, Kim and Verhaege, Marc},
  issn         = {0010-938X},
  journal      = {CORROSION SCIENCE},
  keyword      = {STRESS-CORROSION CRACKING,INDUCED BLISTER CRACKING,HIGH-STRENGTH STEEL,INCLUSIONS,Iron,Steel,SEM,Hydrogen embrittlement,Segregation,NUCLEATION,ALUMINUM,PIPELINE STEELS,EMBRITTLEMENT,ABSORPTION,MECHANISM},
  language     = {eng},
  number       = {10},
  pages        = {3166--3176},
  title        = {Internal and surface damage of multiphase steels and pure iron after electrochemical hydrogen charging},
  url          = {http://dx.doi.org/10.1016/j.corsci.2011.05.060},
  volume       = {53},
  year         = {2011},
}

Altmetric
View in Altmetric
Web of Science
Times cited: